Fich done teknik
| Kategori | Mezi | Valè | Metòd |
| Pwopriyete jeneral yo | Pwen k ap fonn poud (DSC) | 186° C/367° F | ASTM D3418 |
| Gwosè patikil | 58 μm | ASTM D3451 | |
| Dansite esansyèl nan poud | 0.48 g/cm3/0.017 lb/in3 | ASTM D1895 | |
| Dansite nan pati yo | 1.3 g/cm3/0.047 lb/in3 | ASTM D792 | |
| Pwopriyete mekanik | Fòs rupture, max load7, XY, XZ, YX, YZ | 30 MPa/4351 psi | ASTM D638 |
| Fòs rupture, max load7, ZX, XY | 30 MPa/4351 psi | ASTM D638 | |
| Modil tensile7, XY, XZ, YX, YZ | 2500 MPa/363 ksi | ASTM D638 | |
| Modil tensile7, ZX, XY | 2700 MPa/392 ksi | ASTM D638 | |
| Allongement nan break7, XY, XZ, YX, YZ | 10% | ASTM D638 | |
| Elongasyon nan break7, ZX, XY | 10% | ASTM D638 | |
| Fòs flexural (@ 5%),8 XY, XZ, YX, YZ | 57.5 MPa/8340 psi | ASTM D790 | |
| Fòs flexural (@ 5%),8 ZX, XY | 65 MPa/9427 psi | ASTM D790 | |
| Flexural modil, 8 XY, XZ, YX, YZ | 2400 MPa/348 ksi | ASTM D790 | |
| Flexural modil, 8 ZX, XY | 2700 MPa/392 ksi | ASTM D790 | |
| Izod enpak antay (@ 3.2 mm, 23ºC), XY, XZ, YX, YZ, ZX, ZY | 3 KJ/m2 | ASTM D256Metòd tès A | |
| Shore dureté D, XY, XZ, YX, YZ, ZX, ZY | 82 | ASTM D2240 | |
| Pwopriyete tèmik | Tanperati defleksyon chalè (@ 0.45 MPa, 66 psi), XY, XZ, YX, YZ | 174° C/345° F | ASTM D648Metòd tès A |
| Tanperati devyasyon chalè (@ 0.45 MPa, 66 psi), ZX, XY | 175° C/347° F | ASTM D648Metòd tès A | |
| Tanperati defleksyon chalè (@ 1.82 MPa, 264 psi), XY, XZ, YX, YZ | 114° C/237° F | ASTM D648Metòd tès A | |
| Tanperati devyasyon chalè (@ 1.82 MPa, 264 psi), ZX, XY | 120° C/248° F | ASTM D648Metòd tès A | |
| Reyabilite | Rapò minimòm rafrechisman pou pèfòmans ki estab | 30% | |
| Kondisyon anviwònman yo rekòmande | Rekòmande imidite relatif | 50-70% RH | |
| Sètifikasyon | UL 94, UL 746A, RoHS,9 REACH, PAHs |