Okuhle Kakhulu Okungafihli kwe-SLA Resin PMMA njenge-KS158T2e

Incazelo emfushane:

Uhlolojikelele Lwempahla
I-KS158T iyinhlaka ye-SLA esobala ngokubonakalayo ukuze ikhiqize ngokushesha izingxenye ezicacile, ezisebenzayo nezinembile ngokubonakala kwe-acrylic.Kuyashesha ukwakha futhi kulula ukuyisebenzisa.Uhlelo lokusebenza oluhle kakhulu imihlangano esobala, amabhodlela, amashubhu, amalensi ezimoto, izingxenye zokukhanyisa, ukuhlaziya ukugeleza koketshezi nokunye, kanye nama-funcitonal prototypes aqinile.


Imininingwane Yomkhiqizo

Omaka bomkhiqizo

I-datasheet yobuchwepheshe

- Obala Excellent

- Umswakama omuhle kakhulu nokumelana nomswakama

- Kuyashesha ukwakha futhi kulula ukuqeda

- Inembile futhi izinzile

Izicelo Ezikahle

- Amalensi ezimoto

- Amabhodlela namashubhu

- Ama-prototypes asebenzayo aqinile

- Amamodeli wokubonisa esobala

- Ukuhlaziywa kokugeleza kwamanzi

1

Ishidi ledatha yezobuchwepheshe

I-Liquid Properties

Izakhiwo ze-Optical

Ukubukeka Kucace Dp 0.135-0.155 mm
I-Viscosity 325 -425cps @ 28 ℃ Ec 9-12 mJ/cm2
Ukuminyana 1.11-1.14g/cm3 @ 25 ℃ Ugqinsi lwesendlalelo sokwakha 0.1-0.15mm
Izakhiwo Zemishini I-UV Postcure
ISILINGANISO INDLELA YOKUHLOLA VALUE
Ukuqina, Shore D I-ASTM D 2240 72-78
Flexural modulus, Mpa I-ASTM D790 2,680-2,775
Amandla e-Flexural , Mpa I-ASTM D790 65-75
I-tensile modulus, i-MPa I-ASTM D638 2,170-2,385
Amandla aqinile, i-MPa I-ASTM D638 25-30
Ukwandisa ngesikhathi sekhefu I-ASTM D638 12 -20%
Amandla omthelela, i-notched lzod, J/m I-ASTM D 256 58-70
Izinga lokushisa lokuphambuka kokushisa, ℃ I-ASTM D 648 @66PSI 50-60
Ukuguqulwa kwengilazi, Tg I-DMA, E”peak 55-70
Ukuminyana , g/cm3   1.14-1.16

Izinga lokushisa elinconyiwe lokucubungula nokugcinwa kwe-resin engenhla kufanele libe ngu-18 ℃-25 ℃.
Idatha engenhla isekelwe olwazini lwethu lwamanje nolwazi, amanani ayo angase ahluke futhi ancike ekucutshungulweni komshini ngamunye kanye nezinqubo zokuphulukisa ngemva kokwelapha.Idatha yokuphepha enikezwe ngenhla ingeyezinjongo zolwazi kuphela futhi
ayihlanganisi i-MSDS ebopha ngokusemthethweni.