Okudumile kwe-3D Print SLA Resin ABS njengoBrown KS908C

Incazelo emfushane:

Uhlolojikelele Lwempahla

I-KS908C inhlaka ye-SLA enombala onsundu yezingxenye ezinembile nezinemininingwane. Ngokwakheka okuhle, ukumelana nezinga lokushisa namandla amahle, i-KS908C ithuthukiswe ngokukhethekile ukuphrinta i-maquette yezicathulo kanye namamodeli ayinhloko wezicathulo, kanye nesikhunta esisheshayo se-PU sole, kodwa futhi idumile ngamazinyo, ubuciko nokuklama, isifanekiso, upopayi nefilimu.

Thumela i-imeyili kithi Ukulanda Ishidi Ledatha

Imininingwane Yomkhiqizo

Omaka bomkhiqizo

Izinzuzo

- Inembile kakhulu

- Fine surface texture

- Sula imiphetho namakhona

- Ukumelana nomswakama omuhle

Izicelo Ezikahle

- Amamodeli ezicathulo

- Amazinyo

- Ubuciko kanye nomklamo

- Isifanekiso

- Animation ifilimu

Ishidi ledatha yezobuchwepheshe

I-Liquid Properties		Izakhiwo ze-Optical
Ukubukeka	Brown	I-Dp	0.135-0.155 mm
I-Viscosity	405-505 cps @ 28 ℃	Ec	9-12 mJ/cm2
Ukuminyana	1.11-1.14g/cm3 @ 25 ℃	Ugqinsi lwesendlalelo sokwakha	0.1-0.15mm

Izakhiwo Zemishini		I-UV Postcure
ISILINGANISO	INDLELA YOKUHLOLA	VALUE
Ukuqina , Shore D	I-ASTM D 2240	74-80
Flexural modulus , Mpa	I-ASTM D790	2,650-2,750
Amandla e-Flexural , Mpa	I-ASTM D790	60-75
I-tensile modulus, i-MPa	I-ASTM D638	2,150-2,370
Amandla aqinile, i-MPa	I-ASTM D638	25-30
Ukwandisa ngesikhathi sekhefu	I-ASTM D638	12 -20%
Amandla omthelela, i-notched lzod, J/m	I-ASTM D 256	58-70
Izinga lokushisa lokuphambuka kokushisa, ℃	I-ASTM D 648 @66PSI	58-68
Ukuguqulwa kwengilazi, Tg	I-DMA, E”peak	55-70
Ukuminyana , g/cm3		1.14-1.16