Kauntungannana
- Kakuatan anu luhur sareng kateguhan anu kuat
- Akurat jeung diménsi stabil
- Résistansi suhu anu saé
- résistansi Uap alus
Aplikasi idéal
- Modél fungsional kedah tangguh
- Modél konseptual
- model produksi volume low
- Otomotif, aerospace, arsitéktur, aplikasi éléktronik
Téknis Data-lambar
| Pasipatan cair | Pasipatan optik | ||
| Penampilan | konéng lampu | Dp | 0,135-0,155 mm |
| Viskositas | 355-455 cps @ 28 ℃ | Ec | 9-12 mJ/cm2 |
| Kapadetan | 1.11-1.14g/cm3 @ 25 ℃ | Ketebalan lapisan wangunan | 0,05 ~ 0,15 mm |
| Sipat mékanis | UV Postcure | |
| PANGUKURAN | METODE UJI | NILAI |
| Teuas, Shore D | ASTM D 2240 | 76-82 |
| Modulus lentur, Mpa | ASTM D 790 | 2.650-2.760 |
| Kakuatan lentur, Mpa | ASTM D 790 | 65-74 |
| modulus tegangan, MPa | ASTM D 638 | 2.160-2.360 |
| Kakuatan tensile, MPa | ASTM D 638 | 25-30 |
| Elongation dina putus | ASTM D 638 | 12 -20% |
| Kakuatan dampak, notched lzod, J/m | ASTM D 256 | 58 - 70 |
| Suhu defleksi panas, ℃ | ASTM D 648 @66PSI | 58-68 |
| Transisi kaca, Tg | DMA, E'puncak | 55-70 |
| Kapadetan, g/cm3 | 1.14-1.16 | |
Suhu anu disarankeun pikeun ngolah sareng neundeun résin di luhur kedah 18 ℃ -25 ℃.