| UP 5690-W or-K POLYOL | UP 5690 ISOCYANATE | UP 5690 C | MIXED | ||
| Komposisi | Poliol | Isosianat | Poliol | ||
| Campur rasio ku beurat | 100 | 100 | 0 - 50 | ||
| Aspék | cair | cair | cair | cair | |
| Warna | W= BodasK= Hideung | Teu warnaan | Susu bodas | AW / B / C = Bodas AK / B / C = Hideung | |
| Viskositas dina 23°C (mPa.s) | BROOKFIELD LVT | 1000 - 1500 | 140 - 180 | 4500 - 5000 | 500 - 700 |
| Viskositas dina 40°C (mPa.s) | BROOKFIELD LVT | 400 - 600 | - | 2300 - 2500 | 300 - 500 |
| Gravitasi spésifik dina 25°Cgravitasi spésifik kapok produk dina 23 ° C | ISO 1675:1975 ISO 2781:1988 | 1.06- | 1.15- | 1.06- | -1.13 |
| Kahirupan pot dina 25 ° C dina 100 g (mnt) | 10 - 15 | ||||
| Kahirupan pot dina 40 ° C dina 100 g (mnt) | 5 - 7 |
KONDISI PROSES (Mesin tuang vakum)
• Preheat isocyanate ka 23 - 30°C bisi disimpen di handap 20°C.
• Preheat polyol jeung bagian C nepi ka 40 ° C saméméh ngagunakeun.Perlu aduk poliol dugi warna sareng aspekna janten homogen.
• Beurat komponén nurutkeun rasio Pergaulan, nempatkeun isocyanate kana cangkir luhur, tambahkeun bagian C dina polyol mun premix.
• Tuang isosianat kana polyol (ngandung Bagian C) jeung mix pikeun 1 - 2 menit sanggeus degassing salila 10 menit misah.
• Tuang dina vakum dina kapang silicone preheated ka 70 ° C.
• Demould sanggeus 60 - 90 menit dina 70 ° C (Beuki Bagian C dipaké, waktu demoulding leuwih panjang diperlukeun).
| A/B/C | 100/100/0 | 100/100/20 | 100/100/30 | 100/100/50 | ||
| Teu karasa | ISO 868: 2003 | Pesisir D | 83 | 80 | 78 | 75 |
| Kakuatan regangan | ISO 527: 1993 | MPa | 35 | 30 | 28 | 25 |
| Kakuatan flexural | ISO 178: 2001 | MPa | 50 | 35 | 30 | 20 |
| Modulus lentur | ISO 178: 2001 | MPa | 1300 | 1000 | 900 | 600 |
| Elongation dina putus | ISO 527: 1993 | % | 50 | 60 | 65 | 90 |
| kakuatan dampak(CHARPY) Teu kacatur spésimén | ISO 179/2D : 1994 | KJ/m2 | 100 | 90 | 85 | 75 |
| A/B/C | 100/100/0 | 100/100/20 | 100/100/30 | 100/100/50 | ||
| Suhu transisi kaca (Tg) | (1) | °C | 85 | 78 | 75 | 65 |
| shrinkage linier | % | 0.35 | 0.35 | 0.35 | 0.35 | |
| Waktu demoulding (2 - 3mm) dina 70°C | min | 60 - 90 | ||||
Rata-rata nilai-nilai diala on standar spésimén / Ngerasan 16hr at 80°C sanggeus demoulding.
Nanganan Precautions
Pancegahan kaséhatan sareng kaamanan normal kedah diperhatoskeun nalika nanganan produk ieu:
Pastikeun ventilasi alus
Anggo sarung tangan, kacamata kaamanan sareng baju pelindung.
Kanggo inpo nu leuwih lengkep, mangga tingali lambar data kaamanan produk.
Kaayaan Panyimpenan
Kahirupan rak nyaéta 6 bulan di tempat anu garing sareng dina wadah anu henteu dibuka aslina dina suhu antara 15 sareng 25 ° C. Kaleng anu kabuka kedah ditutup pageuh dina simbut nitrogén garing.