SLA Resin Rubber dị ka White ABS dị ka KS198S

Nkọwa dị mkpirikpi:

Nchịkọta ihe
KS198S bụ resin SLA na-acha ọcha, na-agbanwe agbanwe nwere njiri ike dị elu, ngbanwe dị elu na mmetụ dị nro. Ọ dị mma maka ibipụta ụdị akpụkpọ ụkwụ, mkpuchi roba, ụdị biomedical na rọba ndị ọzọ dị ka akụkụ.

Zitere anyị email Budata mpempe akwụkwọ data

Nkọwa ngwaahịa

Mkpado ngwaahịa

Uru

- Mgbanwe dị elu

- Ezigbo mgbochi anya mmiri

- Oke ziri ezi

- Ọmarịcha agba ọcha

Ngwa dị mma

- Akpụkpọ ụkwụ

- Prototypes chọrọ roba dị ka ihe

- Ụdị ngosi ngosi dị nro

Njirimara Liquid

Ọdịdị	Ọcha	Dp	13.5mJ/cm2	[mkpughe dị mkpa]
Viscosity	560 cps @ 30 ℃	Ek	0.125 mm	[slope of cure-depth vs. Na (E) mgbanaka]
Njupụta	1.1 g/cm3	Ụlọ oyi akwa ọkpụrụkpụ	0.08-0.12 mm

Ihe eji arụ ọrụ		UV Postcure
Nhazi	UZỌ anwale	URU
Ike siri ike, Shore D	ASTM D2240	72-78
Mgbanwe mgbanwe , Mpa	ASTM D790	2,680-2,775
Ike mgbanwe , Mpa	ASTM D790	65-75
modul tensile, MPa	ASTM D638	2,170-2,385
Ike tensile, MPa	ASTM D638	25-30
Elongation na ezumike	ASTM D638	12-20%
Ike mmetụta, ọpụrụiche lzod, J/m	ASTM D256	58-70
Okpomọkụ mgbapụ, ℃	ASTM D 648 @66PSI	50-60
Ntugharị iko, Tg	DMA,E” kacha	55-70
Njupụta, g/cm3		1.14-1.16