Takaitaccen Bayani:

Bayanin Kayan Aiki
KS198S farar fata ne, resin SLA mai sassauƙa tare da fasalulluka na babban tauri, babban ƙarfi da taɓawa mai laushi.Yana da manufa don buga samfurin takalma, kunsa na roba, samfurin biomedical da sauran nau'in roba kamar sassa.


Cikakken Bayani

Tags samfurin

Amfani

- Babban sassauci

- Kyakkyawan juriya na hawaye

- Daidai sosai

- Kyakkyawan launi mai kyau

Ingantattun Aikace-aikace

- Kayan takalma

- Samfuran suna buƙatar roba kamar abu

- Samfuran nunin fararen fata masu laushi

1 (3)

Abubuwan Ruwa

Bayyanar Fari Dp 13.5mJ/cm2 [bayani mai mahimmanci]
Dankowar jiki 560 cps@30 ℃ Ec 0.125 mm [zurfin magani vs. A (E) lankwasa]
Yawan yawa 1.1 g/cm 3 Gine-gine kauri 0.08-0.12 mm  
Kayayyakin Injini UV Postcure
AUNA HANYAR GWADA DARAJA
Hardness, Shore D Saukewa: ASTM D2240 72-78
Modules mai sassauci , Mpa Farashin ASTM D790 2,680-2,775
Ƙarfin sassauƙa , Mpa Farashin ASTM D790 65-75
Modules tensile, MPa Saukewa: ASTM D638 2,170-2,385
Ƙarfin ɗaure, MPa Saukewa: ASTM D638 25-30
Tsawaitawa a lokacin hutu Saukewa: ASTM D638 12-20%
Ƙarfin tasiri, ƙwanƙwasa lzod, J/m Bayani na ASTM D256 58-70
Zafin karkatar da zafi, ℃ ASTM D 648 @ 66PSI 50-60
Canjin Gilashi, Tg DMA, E” kololuwa 55-70
Yawan yawa, g/cm3   1.14-1.16

Yawan zafin jiki da aka ba da shawarar don aiki da ajiya na guduro na sama yakamata ya zama 18 ℃-25 ℃.