Foardiel
- Hege fleksibiliteit
- Goed tearresistinsje
- Hiel akkuraat
- Prachtige wite kleur
Ideale applikaasjes
- Schoeisel
- Prototypen hawwe rubber lykas materiaal nedich
- Sêfte wite displaymodellen
Liquid Eigenskippen
| Ferskining | Wyt | Dp | 13,5 mJ/cm2 | [krityske eksposysje] |
| Viskositeit | 560 cps @ 30 ℃ | Ec | 0.125 mm | [helling fan úthardingsdjipte tsjin yn (E) kromme] |
| Tichtheid | 1,1 g/cm3 | Bouwe laach dikte | 0,08-0,12 mm |
| Meganyske eigenskippen | UV Postcure | |
| MJITTING | TEST METOADE | WEARDE |
| Hardheid, Shore D | ASTM D 2240 | 72-78 |
| Flexural modulus, Mpa | ASTM D 790 | 2.680-2.775 |
| Flexural sterkte, Mpa | ASTM D 790 | 65- 75 |
| Tensile modulus, MPa | ASTM D 638 | 2.170-2.385 |
| Treksterkte, MPa | ASTM D 638 | 25-30 |
| Ferlinging by brek | ASTM D 638 | 12 -20% |
| Impact sterkte, kerf lzod, J/m | ASTM D 256 | 58 - 70 |
| Heat deflection temperatuer, ℃ | ASTM D 648 @66PSI | 50-60 |
| Glêzen oergong, Tg | DMA, E" peak | 55-70 |
| Tichtens, g/cm3 | 1.14-1.16 | |
Oanrikkemandearre temperatuer foar ferwurking en opslach fan 'e boppesteande hars moat 18 ℃ -25 ℃ wêze.